Cavitation reduction is not as simple as blocking off a couple cavities and continuing to run. The process should be as close as possible to the original process, but this will require an adjustment to the process inputs. Question: Do you have a good process for blocking cavities? My Response: The process is almost identical […]
Monthly Archives
February 2016
PVC Packing vs. Thin Wall Molding
Thin wall molding is a relative term that implies the flow length is long with respect to the part thickness and material viscosity… Question: Our thick PVC parts require a higher packing pressure than the injection pressure, yet the training states this is typically the case for thin-wall molding. In our case, the parts are […]